“Liquid Mould” – Casting Liquid Silicone Rubber, 5-40 Shores, Bi-Component A B

TECHNICAL DATA “LIQUID MOULD” – Casting Liquid Silicone Rubber – 15/20 ShoresMix ratio: 100: 5 in weight (= 2%)Pot Life: 60-80 minViscosity: 26000 mPas (15 shores) / 10000 mPas (20 shores)Pouring time: 60-80 minDemould time: 12 hoursHardness: 20 -3 Shore A; 15 -3 Shore AShores – Higher values indicate higher hardness, lower – softer mould you get.“LIQUID MOULD” – Casting Liquid Silicone Rubber – 5 ShoresType: Condensation-cure liquid silicone rubber (casting type) Mixing Ratio: 100:5 (by weight) Hardness: 5 Shore A (after 24 hours) Appearance Before Curing: Viscous liquid Appearance After Curing: Elastic rubber Color: Component A: White Component B: Transparent Specific Gravity: 1.200 Kg/l ± 0.020 Viscosity: 10,000 – 30,000 CpS Pot Life: 30–60 minutes Demolding Time: 24 hours Shore A Hardness: 05 ± 2 (DIN 53505) Tear Strength: 16 N/mm ± 0.5 (ASTM D 624 Type B) Tensile Strength: 4.0 N/mm² ± 0.5 (DIN 53504 – Type S A 3) Elongation at Break: 900% ± 30 (DIN 53504 – Type S A 3) Linear Shrinkage: Max 0.5% after 5 days (ISO 4823) Flame Resistance: Self-extinguishing (ASTM 1692)“LIQUID MOULD” – Casting Liquid Silicone Rubber – 30 Shores✔️ STRONG AND DURABLE Shore A hardness of 30±2, ideal for supporting heavy materials such as concrete, resins, and plaster. ✔️ HIGH PRECISION Optimized viscosity (Part A: 23,000±2,000 mPa·s) for uniform material distribution. ✔️ TECHNICAL TIMINGS Working time (WT): 30–40 minutes Curing time: 8–10 hours Technical Parameters: Color Part A: White Color Part B: Transparent/light yellow Shore A Hardness: 30±2 Working Time (WT): 30–40 minutes Curing Time: 8–10 hours at 25°C Tear Strength: 25 kN/m Elongation: 350%“LIQUID MOULD” – Casting Liquid Silicone Rubber – 40 Shores SUPERIOR RESISTANCEShore A hardness of 38±2 ensures repeated use and resistance to aggressive materials. ✔️ ROBUST DESIGN High viscosity (Part A: 24,000±2,000 mPa·s) ensures greater dimensional stability of the mold. ✔️ TECHNICAL TIMINGS Working time (WT): 30–40 minutes Curing time: 8–10 hours Technical Parameters: Color Part A: White Color Part B: Transparent/light yellow Shore A Hardness: 38±2 Working Time (WT): 30–40 minutes Curing Time: 8–10 hours at 25°C Tear Strength: 19 kN/m Elongation: 300%